- 密度 [g/cm3]: 0.0961
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0961 g/cc | 0.00347 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 5.00 MPa | >= 725 psi | Bare, min, preliminary value obtained from limited testing |
| >= 5.38 MPa | >= 780 psi | Stabilized, min, preliminary value obtained from limited testing | |
| 6.65 MPa | 965 psi | Bare, typ, preliminary value obtained from limited testing | |
| 7.17 MPa | 1040 psi | Stabilized, typ, preliminary value obtained from limited testing | |
| Shear Modulus | 0.0552 GPa | 8.00 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.0931 GPa | 13.5 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 1.24 MPa | >= 180 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 1.65 MPa | 240 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 2.00 MPa | >= 290 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 2.69 MPa | 390 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |