- 吸水率 [%]: 0.1
- 缺口冲击强度: 7.47
- 弯曲强度 [MPa]: 62.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 - 1.77 g/cc | 1.70 - 1.77 g/cc | |
| Water Absorption | 0.10 - 0.30 % | 0.10 - 0.30 % | 24 hours, 23°C |
| Linear Mold Shrinkage | 0.00 - 0.0010 cm/cm | 0.00 - 0.0010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 55 - 65 | 55 - 65 | |
| Tensile Strength, Ultimate | 62.1 - 82.7 MPa | 9000 - 12000 psi | |
| Flexural Strength | 179 - 214 MPa | 26000 - 31000 psi | |
| Compressive Strength | 159 - 193 MPa | 23000 - 28000 psi | |
| Izod Impact, Notched | 7.47 - 10.1 J/cm | 14.0 - 19.0 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 14.2 kV/mm | 360 kV/in | Short Time |
| Arc Resistance | >= 180 sec | >= 180 sec | |
| Comparative Tracking Index | >= 500 V | >= 500 V | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-0 @Thickness 6.35 mm | V-0 @Thickness 0.250 in | ||
| V-0 @Thickness 3.17 mm | V-0 @Thickness 0.125 in | ||
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 138 - 166 °C | 280 - 330 °F | |