- 密度 [g/cm3]: 1.2
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 - 1.40 g/cc | 0.0434 - 0.0506 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 800 - 1000 MPa | 116000 - 145000 psi | Longitudinal | ||
| Elongation at Break | 2.5 % | 2.5 % | Longitudinal | ||
| Flexural Strength | 150 - 250 MPa | 21800 - 36300 psi | Longitudinal | ||
| Flexural Modulus | 17.0 - 22.0 GPa | 2470 - 3190 ksi | Longitudinal | ||
| Compressive Strength | 100 - 300 MPa | 14500 - 43500 psi | Longitudinal | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | |||
| Descriptive Properties | |||||
| Volume Fraction Fibers, % | 50-60 | ||||