- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |
| Linear Mold Shrinkage | 0.00040 cm/cm | 0.00040 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 65.0 MPa | 9430 psi | ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | Tangent; ASTM D790 |
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Poissons Ratio | 0.30 | 0.30 | |
| Izod Impact, Unnotched | 9.00 J/cm | 16.9 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 270 °C | >= 518 °F | ASTM D648 |
| Glass Transition Temp, Tg | 182 °C | 360 °F | ASTM D4065-01 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Injection, Injection-Compression or Compression Molding |
| Clamp Pressure | <= 6.89 MPa | <= 1000 psi | Molding Pressure |