- 弯曲模量 [MPa]: 38.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | <= 0.00 cm/cm | <= 0.00 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 282 MPa | 40900 psi | ASTM D638 | ||
| Tensile Modulus | 55.0 GPa | 7980 ksi | ASTM D638 | ||
| Flexural Strength | 606 MPa | 87900 psi | ASTM D790 | ||
| Flexural Modulus | 38.5 GPa | 5580 ksi | ASTM D790 | ||
| Compressive Strength | 286 MPa | 41500 psi | ASTM D695 | ||
| Compressive Modulus | 33.8 GPa | 4900 ksi | ASTM D695 | ||
| Poissons Ratio | 0.305 | 0.305 | ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 287 °C | 549 °F | Deflection Temperature, Load not specified; ASTM D648 | ||
| Glass Transition Temp, Tg | 118 °C | 244 °F | ASTM D4065 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 127 - 154 °C | 260 - 310 °F | Compression Molding | ||
| Cure Time | 5.00 - 10.0 min @Temperature 138 °C | 0.0833 - 0.167 hour @Temperature 280 °F | |||
| Shelf Life | 2.00 Month @Temperature 23.9 °C | 2.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Fiber Length (in) | 1 | Carbon, nominal | |||