- 密度 [g/cm3]: 1.75
- 缺口冲击强度: 16.0
- 断裂伸长率 [%]: 413
- 弯曲强度 [MPa]: 213.0
- 弯曲模量 [MPa]: 15.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 213 MPa | 30900 psi | ASTM D638 |
| Flexural Yield Strength | 413 MPa | 59900 psi | ASTM D790 |
| Flexural Modulus | 15.8 GPa | 2290 ksi | ASTM D790 |
| Compressive Yield Strength | 246 MPa | 35700 psi | ASTM D695 |
| Izod Impact, Notched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 145 °C | 293 °F | DMA, ASTM D4065 |
| Shrinkage | <= 0.0010 % | <= 0.0010 % | ASTM D955 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 127 - 160 °C | 261 - 320 °F | Mold temperature |