- 吸水率 [%]: 0.11
- 弯曲模量 [MPa]: 77.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00 cm/cm | 0.00 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 993 MPa | 144000 psi | ASTM D638 |
| Tensile Modulus | 94.5 GPa | 13700 ksi | ASTM D638 |
| Flexural Strength | 1310 MPa | 190000 psi | ASTM D790 |
| Flexural Modulus | 77.9 GPa | 11300 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 287 °C | 549 °F | Deflection Temperature, Load not specified; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C @Thickness 12.7 mm | 270 - 300 °F @Thickness 0.500 in | Compression Molding |
| Clamp Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C | 0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F | |
| Shelf Life | 3.00 Month @Temperature 23.9 °C | 3.00 Month @Temperature 75.0 °F | |