- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.1
- 缺口冲击强度: 19.2
- 断裂伸长率 [%]: 585
- 弯曲强度 [MPa]: 344.0
- 弯曲模量 [MPa]: 20.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 Hrs. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 70 | 70 | ASTM D2583 |
| Tensile Strength, Ultimate | 344 MPa | 49900 psi | ASTM D638 |
| Tensile Modulus | 26.1 GPa | 3790 ksi | ASTM D638 |
| Flexural Yield Strength | 585 MPa | 84800 psi | ASTM D790 |
| Flexural Modulus | 20.6 GPa | 2990 ksi | ASTM D790 |
| Compressive Yield Strength | 289 MPa | 41900 psi | ASTM D695 |
| Compressive Modulus | 18.6 GPa | 2700 ksi | ASTM D695 |
| Izod Impact, Notched | 19.2 J/cm | 36.0 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+12 ohm-cm | >= 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 12.0 kV/mm | 305 kV/in | ASTM D149 |
| Arc Resistance | 129 sec | 129 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 °C | 8.61 µin/in-°F @Temperature 68.0 °F | TMA |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Deflection Temp; Load not reported; ASTM D648 |
| Shrinkage | 0.00 % | 0.00 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C | 270 - 300 °F | Mold temperature |
| Shelf Life | 2.00 Month @Temperature 23.9 °C | 2.00 Month @Temperature 75.0 °F | |