- 密度 [g/cm3]: 1.85
- 吸水率 [%]: 0.25
- 缺口冲击强度: 8.5
- 弯曲强度 [MPa]: 83.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | 24 hrs.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 68 | 68 | |
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 170 MPa | 24700 psi | ASTM D695 |
| Izod Impact, Notched | 8.50 J/cm | 15.9 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.70e+14 ohm-cm | 5.70e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.4 @Frequency 60 Hz | 4.4 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Arc Resistance | 188 sec | 188 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.26 J/g-°C | 0.300 BTU/lb-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 5V |