- 缺口冲击强度: 11.0
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |
| Filler Content | 38 % | 38 % | Glass, weight fraction; Premix washout |
| Linear Mold Shrinkage | 0.00025 cm/cm | 0.00025 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Izod Impact, Notched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.0 J/cm | 28.1 ft-lb/in | ASTM D4812 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |