Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC

Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC 物性表: Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC物性表及特性介绍,Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC注塑参数详情,如需Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC下载, 可到相关下载区下载
  • 吸水率 [%]: 0.2
  • 缺口冲击强度: 13.9
  • 弯曲强度 [MPa]: 82.7
  • 弯曲模量 [MPa]: 11.7
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.83 g/cc1.83 g/ccASTM D792
Water Absorption 0.20 %0.20 %ISO 62
Linear Mold Shrinkage 0.00050 cm/cm0.00050 in/inISO 2577
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 82.7 MPa12000 psiISO 527
Tensile Modulus 13.8 GPa2000 ksitangent; ISO 527
Flexural Strength 179 MPa26000 psiISO 178
Flexural Modulus 11.7 GPa1700 ksiTangent; ISO 178
Compressive Strength 310 MPa45000 psiASTM D695
Poissons Ratio 0.330.33ISO 527
Shear Modulus 5.19 GPa753 ksiCalculated
Izod Impact, Notched 13.9 J/cm26.0 ft-lb/inASTM D256
 
Thermal PropertiesMetricEnglishComments
CTE, linear 36.0 µm/m-°C
@Temperature 20.0 °C
20.0 µin/in-°F
@Temperature 68.0 °F
Z-direction; ASTM D696
CTE, linear, Transverse to Flow 27.0 µm/m-°C
@Temperature 20.0 °C
15.0 µin/in-°F
@Temperature 68.0 °F
XY-direction; ASTM D696
Specific Heat Capacity 1.51 J/g-°C0.360 BTU/lb-°FASTM D1269E
Thermal Conductivity 0.300 W/m-K2.08 BTU-in/hr-ft²-°FASTM D1269E
Deflection Temperature at 1.8 MPa (264 psi) 271 °C520 °FASTM D648
Glass Transition Temp, Tg 188 °C370 °FASTM D4065-01

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-33519.html

免责声明: 本文 Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4