Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC

Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC 物性表: Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC物性表及特性介绍,Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC注塑参数详情,如需Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC下载, 可到相关下载区下载
  • 吸水率 [%]: 0.2
  • 弯曲强度 [MPa]: 86.2
  • 弯曲模量 [MPa]: 6.21
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.80 g/cc1.80 g/ccASTM D792
Water Absorption 0.20 %0.20 %ISO 62
Linear Mold Shrinkage 0.00026 cm/cm0.00026 in/inISO 2577
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 86.2 MPa12500 psiISO 62
 58.6 MPa
@Temperature 150 °C
8500 psi
@Temperature 302 °F
ISO 62
Tensile Modulus 15.2 GPa2200 ksitangent; ISO 527
 8.27 GPa
@Temperature 150 °C
1200 ksi
@Temperature 302 °F
ISO 527
Flexural Strength 176 MPa25500 psiISO 178
 121 MPa
@Temperature 150 °C
17500 psi
@Temperature 302 °F
ISO 178
Flexural Modulus  6.21 GPa
@Thickness 2.50 mm,
Temperature 150 °C
900 ksi
@Thickness 0.0984 in,
Temperature 302 °F
Secant; ISO 178
 8.27 GPa
@Thickness 2.50 mm,
Temperature 22.0 °C
1200 ksi
@Thickness 0.0984 in,
Temperature 71.6 °F
Secant; ISO 178
 8.27 GPa
@Thickness 0.500 mm,
Temperature 150 °C
1200 ksi
@Thickness 0.0197 in,
Temperature 302 °F
Secant; ISO 178
 11.7 GPa
@Thickness 0.500 mm,
Temperature 22.0 °C
1700 ksi
@Thickness 0.0197 in,
Temperature 71.6 °F
Secant; ISO 178
Izod Impact, Unnotched 12.8 J/cm24.0 ft-lb/inASTM D4812
Impact 0.230.23(in) High Speed Impact (Deflection Max Load); ISO 6603-2
 517517(lb) High Speed Impact (Impact Max Load); ISO 6603-2
Impact Test 6.91 J5.10 ft-lbHigh Speed Impact (Energy Max Load); ISO 6603-2
 12.6 J9.30 ft-lbHigh Speed Impact (Total Energy); ISO 6603-2
 
Thermal PropertiesMetricEnglishComments
CTE, linear 27.0 µm/m-°C
@Temperature 20.0 °C
15.0 µin/in-°F
@Temperature 68.0 °F
Z-direction; ASTM D696
CTE, linear, Transverse to Flow 18.0 µm/m-°C
@Temperature 20.0 °C
10.0 µin/in-°F
@Temperature 68.0 °F
XY-direction; ASTM D696
Thermal Conductivity 0.550 W/m-K3.82 BTU-in/hr-ft²-°FASTM 1530-93
Glass Transition Temp, Tg 188 °C370 °FISO 6721 DMS

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-33528.html

免责声明: 本文 Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4