- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |
| Linear Mold Shrinkage | 0.00075 cm/cm | 0.00075 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 140 MPa | 20300 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ASTM D638 |
| Flexural Strength | 270 MPa | 39200 psi | ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 |
| Poissons Ratio | 0.33 | 0.33 | |
| Shear Modulus | 4.90 GPa | 711 ksi | Calculated |
| Izod Impact, Notched | 10.0 J/cm | 18.7 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 17.0 J/cm | 31.8 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |