- 吸水率 [%]: 0.1
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.82 g/cc | 1.82 g/cc | |
| Water Absorption | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 64.0 MPa @Temperature 150 °C | 9280 psi @Temperature 302 °F | ISO 527 |
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | ISO 527 | |
| Tensile Modulus | 9.30 GPa @Temperature 150 °C | 1350 ksi @Temperature 302 °F | ISO 527 |
| 14.0 GPa @Temperature 23.0 °C | 2030 ksi @Temperature 73.4 °F | ISO 527 | |
| Flexural Strength | 108 MPa @Temperature 150 °C | 15700 psi @Temperature 302 °F | ISO 178 |
| 200 MPa @Temperature 23.0 °C | 29000 psi @Temperature 73.4 °F | ISO 178 | |
| Flexural Modulus | 8.00 GPa @Temperature 150 °C | 1160 ksi @Temperature 302 °F | ISO 178 |
| 13.0 GPa @Temperature 23.0 °C | 1890 ksi @Temperature 73.4 °F | ISO 178 | |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.40 GPa | 783 ksi | Calculated |
| Izod Impact, Unnotched | 13.5 J/cm | 25.3 ft-lb/in | ASTM D4812 |
| Impact | 3.3 | 3.3 | (kN) High Speed Impact (Impact at max load); ISO 6603-2 |
| 4.9 | 4.9 | (mm) High Speed Impact (Deflection at max load); ISO 6603-2 | |
| Impact Test | 7.80 J | 5.75 ft-lb | High Speed Impact (Energy at max load); ISO 6603-2 |
| 18.8 J | 13.9 ft-lb | High Speed Impact (Total energy); ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | 210 °C | 410 °F | ISO 6721 DMS |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |