- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.427
- 弯曲强度 [MPa]: 34.5
- 弯曲模量 [MPa]: 8.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.86 g/cc | 1.86 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | -0.000300 cm/cm | -0.000300 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | ASTM D638 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | tangent; ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790-1 |
| Flexural Modulus | 8.96 GPa @Thickness 0.500 mm, Temperature 150 °C | 1300 ksi @Thickness 0.0197 in, Temperature 302 °F | secant; ASTM D790-1 |
| 11.7 GPa @Thickness 0.500 mm, Temperature 22.0 °C | 1700 ksi @Thickness 0.0197 in, Temperature 71.6 °F | secant; ASTM D790-1 | |
| Poissons Ratio | 0.30 | 0.30 | ISO 527 |
| Shear Modulus | 5.85 GPa | 848 ksi | Calculated |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.854 J/cm | 1.60 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C | 20.0 µin/in-°F @Temperature 68.0 °F | Z-direction; ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature 20.0 °C | 15.0 µin/in-°F @Temperature 68.0 °F | XY-direction; ASTM D696 |
| Specific Heat Capacity | 1.51 J/g-°C | 0.360 BTU/lb-°F | ASTM D1269E |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM D1269E |