- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.1
- 缺口冲击强度: 4.81
- 断裂伸长率 [%]: 124
- 弯曲强度 [MPa]: 51.7
- 弯曲模量 [MPa]: 8.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.85 g/cc | 0.0632 - 0.0668 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 - 0.30 % | 0.10 - 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | Ambient part /mold |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 51.7 - 72.4 MPa | 7500 - 10500 psi | ASTM D638 |
| Modulus of Elasticity | 10.3 - 11.7 GPa | 1500 - 1700 ksi | ASTM D638 |
| Flexural Yield Strength | 124 - 165 MPa | 18000 - 24000 psi | ASTM D790 |
| Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | ASTM D790 |
| Compressive Yield Strength | 159 - 179 MPa | 23000 - 26000 psi | ASTM D695 |
| Izod Impact, Notched | 4.81 - 7.47 J/cm | 9.00 - 14.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.47 - 10.1 J/cm | 14.0 - 19.0 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 47.2 kV/mm | 1200 kV/in | ASTM D149 |
| Arc Resistance | >= 180 sec | >= 180 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| UL RTI, Electrical | 130 °C | 266 °F | U.L. 746 B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | U.L. 746 B |
| Flammability, UL94 | HB @Thickness >=1.47 mm | HB @Thickness >=0.0579 in | |