- 缺口冲击强度: 8.01
- 弯曲强度 [MPa]: 65.5
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 g/cc | 1.78 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00068 cm/cm | 0.00068 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | tangent; ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790-1 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | Tangent; ASTM D790-1 |
| Poissons Ratio | 0.30 | 0.30 | ISO 527 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.2 J/cm | 21.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C | 20.0 µin/in-°F @Temperature 68.0 °F | Z-direction; ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature 20.0 °C | 15.0 µin/in-°F @Temperature 68.0 °F | XY-direction; ASTM D696 |
| Specific Heat Capacity | 0.335 J/g-°C | 0.0800 BTU/lb-°F | ASTM D1269E |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM D1269E |