- 缺口冲击强度: 3.7
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | |||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Polymerization Shrinkage | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 | ||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 | ||
| Poissons Ratio | 0.30 | 0.30 | |||
| Shear Modulus | 3.50 GPa | 508 ksi | Calculated | ||
| Izod Impact, Notched | 3.70 J/cm | 6.93 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D4812 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction | ||
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 150 °C | 302 °F | Compression Molding | ||
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure | ||
| Descriptive Properties | |||||
| Flame Resistance | pass at 3 mm | ANSI Z124.2 | |||
| Stain Resistance | pass | ANSI Z124.2 | |||