- 缺口冲击强度: 8.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 - 1.85 g/cc | 1.70 - 1.85 g/cc | |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 75.0 MPa | 10900 psi | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.60 GPa | 667 ksi | Calculated |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.5 J/cm | 21.5 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |