- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.1
- 缺口冲击强度: 8.2
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | in 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 40 - 50 | 40 - 50 | ASTM D2583 |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 8.20 J/cm | 15.4 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |