- 密度 [g/cm3]: 1.92
- 缺口冲击强度: 9.5
- 断裂伸长率 [%]: 175
- 弯曲强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.92 g/cc | 0.0694 lb/in³ | |
| Water Absorption | <= 0.35 % | <= 0.35 % | ASTM D570-63 |
| Linear Mold Shrinkage | 0.00070 cm/cm | 0.00070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 45 | 45 | ASTM D2583 |
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638-68 |
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790-70 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790-70 |
| Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695-69 |
| Izod Impact, Notched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D256-70 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 13.0 µm/m-°C @Temperature 23.0 - 150 °C | 7.22 µin/in-°F @Temperature 73.4 - 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 235 °C | >= 455 °F | ASTM D648-61 |