- 密度 [g/cm3]: 1.7
- 缺口冲击强度: 11.0
- 断裂伸长率 [%]: 126
- 弯曲强度 [MPa]: 73.0
- 弯曲模量 [MPa]: 6.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | |
| Water Absorption | <= 0.45 % | <= 0.45 % | ASTM D570-63 |
| Linear Mold Shrinkage | 0.00060 cm/cm | 0.00060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 73.0 MPa | 10600 psi | ASTM D638-68 |
| Flexural Yield Strength | 126 MPa | 18300 psi | ASTM D790-70 |
| Flexural Modulus | 6.25 GPa | 906 ksi | |
| Izod Impact, Notched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D256-70 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.1 µm/m-°C @Temperature 23.0 - 150 °C | 5.61 µin/in-°F @Temperature 73.4 - 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 235 °C | >= 455 °F | ASTM D648-61 |
- 关键词:
- 供应
- SMC
- Budd Hi-Flex® SMC