- 密度 [g/cm3]: 1.89
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.2
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D1895 | ||
| Density | 1.89 g/cc | 0.0683 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.090 % @Temperature 23.0 °C, Time 86400 sec | 0.090 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 75 | 75 | ASTM D2583 | ||
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 | ||
| Flexural Strength | 65.0 MPa | 9430 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 | ||
| Compressive Strength | 88.0 MPa | 12800 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 8.10 kV/mm @Frequency 60.0 Hz | 206 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 13.3 kV/mm @Frequency 60.0 Hz | 338 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Arc Resistance | 240 sec | 240 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Red, Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||