- 拉伸强度 [MPa]: 3.45
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | "B" component | ||
| 1.41 g/cc | 1.41 g/cc | "A" component | |||
| Viscosity | 4000 cP | 4000 cP | "B" component | ||
| 4000 cP | 4000 cP | "A" component | |||
| Storage Temperature | <= 38.0 °C | <= 100 °F | 12 months | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | cured 20 mins @ 150°C | ||
| Tensile Strength, Yield | 3.45 MPa | 500 psi | cured 20 mins @ 150°C | ||
| Elongation at Break | 120 % | 120 % | cured 20 mins @ 150°C | ||
| 100% Modulus | 0.00207 GPa | 0.300 ksi | cured 20 mins @ 150°C | ||
| Tear Strength | 3.51 kN/m | 20.0 pli | cured 20 mins @ 150°C | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.47e+15 ohm-cm | 1.47e+15 ohm-cm | |||
| Dielectric Constant | 3.1 @Frequency 1000 Hz | 3.1 @Frequency 1000 Hz | |||
| Dissipation Factor | 0.0030 | 0.0030 | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft²-°F | |||
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 150 °C | 0.250 hour @Temperature 302 °F | |||
| 30.0 min @Temperature 125 °C | 0.500 hour @Temperature 257 °F | ||||
| 45.0 min @Temperature 100 °C | 0.750 hour @Temperature 212 °F | ||||
| Pot Life | >= 480 min | >= 480 min | |||
| Descriptive Properties | |||||
| Color | Beige | "A" component | |||
| Black | "B" component | ||||