- 拉伸强度 [MPa]: 1.72
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.63 g/cc | 1.63 g/cc | "B" component | ||
1.63 g/cc | 1.63 g/cc | "A" component | |||
Viscosity | 6000 cP | 6000 cP | "B" component | ||
6000 cP | 6000 cP | "A" component | |||
Storage Temperature | <= 38.0 °C | <= 100 °F | 12 months | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 45 | 45 | cured 15 mins @ 150°C | ||
Tensile Strength, Yield | 1.72 MPa | 249 psi | cured 15 mins @ 150°C | ||
Elongation at Break | 240 % | 240 % | cured 15 mins @ 150°C | ||
100% Modulus | 1.24 GPa | 180 ksi | cured 15 mins @ 150°C | ||
Tear Strength | 7.89 kN/m | 45.0 pli | cured 15 mins @ 150°C | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 4.02e+14 ohm-cm | 4.02e+14 ohm-cm | |||
Dielectric Constant | 3.1 @Frequency 1000 Hz | 3.1 @Frequency 1000 Hz | |||
Dissipation Factor | 0.0090 | 0.0090 | |||
Comparative Tracking Index | 600 V | 600 V | |||
Thermal Properties | Metric | English | Comments | ||
Thermal Conductivity | 0.680 W/m-K | 4.72 BTU-in/hr-ft²-°F | |||
Maximum Service Temperature, Air | 240 °C | 464 °F | |||
Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
Descriptive Properties | |||||
Color | Beige | "A" component | |||
Black | "B" component | ||||
Work life | 100 mins |