- 拉伸强度 [MPa]: 5.2
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | QSil 216B | ||
| 1.02 g/cc | 1.02 g/cc | QSil 216A | |||
| Viscosity | 500 cP | 500 cP | QSil 216B | ||
| 4000 cP | 4000 cP | QSil 216A | |||
| Linear Mold Shrinkage | <= 0.0010 cm/cm | <= 0.0010 in/in | cured 60 mins @ 100°C | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 | 40 | cured 60 mins @ 100°C | ||
| Tensile Strength, Yield | 5.20 MPa | 754 psi | cured 60 mins @ 100°C | ||
| Elongation at Break | 100 % | 100 % | cured 60 mins @ 100°C | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.70e+15 ohm-cm | 1.70e+15 ohm-cm | |||
| Dielectric Constant | 2.69 @Frequency 1000 Hz | 2.69 @Frequency 1000 Hz | |||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |||
| Dissipation Factor | 0.00060 @Frequency 1000 Hz | 0.00060 @Frequency 1000 Hz | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 275 µm/m-°C @Temperature 20.0 °C | 153 µin/in-°F @Temperature 68.0 °F | |||
| Specific Heat Capacity | 1.26 J/g-°C | 0.301 BTU/lb-°F | |||
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 204 °C | 399 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.406 | 1.406 | cured 60 mins @ 100°C | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 96.0 min | 96.0 min | |||
| Descriptive Properties | |||||
| Color | Clear | QSil 216A | |||
| Clear | QSil 216B | ||||
| Transparent, colorless | Catalyzed | ||||
| Consistency | Easily pourable | Catalyzed | |||