- 拉伸强度 [MPa]: 3.45
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.41 g/cc | 1.41 g/cc | "A" component | ||
1.41 g/cc | 1.41 g/cc | "B" component | |||
Viscosity | 4000 cP | 4000 cP | "A" component | ||
4000 cP | 4000 cP | "B" component | |||
Storage Temperature | <= 38.0 °C | <= 100 °F | 12 months | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 55 | 55 | cured 7 mins @ 150°C | ||
Tensile Strength, Yield | 3.45 MPa | 500 psi | cured 7 mins @ 150°C | ||
Elongation at Break | 120 % | 120 % | cured 7 mins @ 150°C | ||
100% Modulus | 0.00207 GPa | 0.300 ksi | cured 7 mins @ 150°C | ||
Tear Strength | 3.51 kN/m | 20.0 pli | cured 7 mins @ 150°C | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 3.26e+15 ohm-cm | 3.26e+15 ohm-cm | |||
Dielectric Constant | 3.4 @Frequency 1000 Hz | 3.4 @Frequency 1000 Hz | |||
Dissipation Factor | 0.00600 | 0.00600 | |||
Thermal Properties | Metric | English | Comments | ||
Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft²-°F | |||
Maximum Service Temperature, Air | 204 °C | 399 °F | |||
Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
Processing Properties | Metric | English | Comments | ||
Pot Life | >= 30 min | >= 30 min | customized cure available | ||
Descriptive Properties | |||||
Color | Beige | "A" component | |||
Red | "B" component |