- 拉伸强度 [MPa]: 1.38
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.04 g/cc | 1.04 g/cc | Uncatalyzed, DBT Catalyst | ||
1.20 g/cc | 1.20 g/cc | "A" component | |||
1.47 g/cc | 1.47 g/cc | Uncatalyzed, Deep Section Catalyst | |||
Viscosity | 6500 cP | 6500 cP | Uncatalyzed, Deep Section Catalyst | ||
11000 cP | 11000 cP | ||||
Storage Temperature | 4.00 °C | 39.2 °F | 12 months | ||
5.00 - 27.0 °C | 41.0 - 80.6 °F | 3 months | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 40 | 40 | catalyzed 24 hours at room temperature. | ||
Tensile Strength, Yield | 1.38 MPa | 200 psi | catalyzed 24 hours at room temperature | ||
Elongation at Break | 200 % | 200 % | catalyzed 24 hours at room temperature. | ||
Tear Strength | 3.51 kN/m | 20.0 pli | catalyzed 24 hours at room temperature | ||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 204 °C | 399 °F | |||
Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min | 2.00 hour | Tack free time, catalyzed, Deep Section Catalyst | ||
240 min | 4.00 hour | Tack free time, catalyzed, DBT Catalyst | |||
Gel Time | 45.0 min | 45.0 min | catalyzed, DBT Catalyst | ||
70.0 min | 70.0 min | catalyzed, Deep Section Catalyst | |||
Descriptive Properties | |||||
Color | White | ||||
Hegman Grind | 3 |