- 密度 [g/cm3]: 1.15
- 弯曲强度 [MPa]: 4.14
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | A Component; ASTM D1475 |
| 1.15 g/cc | 0.0415 lb/in³ | B Component; ASTM D1475 | |
| Outgassing - Total Mass Loss | 0.55 % | 0.55 % | at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.050 % | 0.050 % | at 10E-6 torr; ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 16 | 16 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 4.14 MPa @Thickness 1.47 mm | 600 psi @Thickness 0.0580 in | Cured; ASTM D638 |
| Elongation at Break | 700 % | 700 % | Cured property; ASTM D638 |
| Adhesive Bond Strength | 2.76 MPa | 400 psi | Al-to-Al Lap Shear; Cured property;5 mil bondline thickness on primed aluminum panels; ASTM D1002 |
| Tear Strength | 23.7 kN/m | 135 pli | ASTM D624 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Cured property; ASTM D257 |
| Dielectric Strength | 13.8 kV/mm @Thickness 6.35 mm | 350 kV/in @Thickness 0.250 in | Cured; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 µm/m-°C @Temperature 20.0 °C | 30.0 µin/in-°F @Temperature 68.0 °F | Cured property; alpha 1 |
| 235 µm/m-°C @Temperature 20.0 °C | 131 µin/in-°F @Temperature 68.0 °F | Cured property; alpha 2 | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Minimum Service Temperature, Air | -110 °C | -166 °F | |
| Glass Transition Temp, Tg | -110 °C | -166 °F | Cured property; Perkin Elmer TMS-2 |
| Flash Point | >= 150 °C | >= 302 °F | A Component; ASTM D92 |
| >= 150 °C | >= 302 °F | B Component; ASTM D92 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Time not defined |
| 65.0 °C | 149 °F | Cure 1 hrs | |
| 100 °C | 212 °F | Cure 0.5 hrs. | |