- 密度 [g/cm3]: 1.35
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.52 MPa | 800 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 225 % | 225 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 15.8 kN/m | 90.0 pli | Die B, ppiw, Silicone Property; ASTM D624 | ||
| Peel Strength | 1.35 kN/m | 7.70 pli | Bond Strength (S2 to S2); Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.5 kV/mm | 469 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 200 °C | 392 °F | E54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | E54153 | ||
| Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length | ||
| <= 15 | <= 15 | [sec] (Flame and Glow Total), Glow Time | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 29.2 | Arlon SQA-TMS-025 | |||
| Uncoated Fabric Break Strength | 300 lb/in | Fill Direction, Substrate Property | |||
| 450 lb/in | Warp Direction, Substrate Property | ||||