- 密度 [g/cm3]: 1.21
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 38.1 microns | 1.50 mil | Interleave 1 | ||
| 38.1 microns | 1.50 mil | Interleave 2 | |||
| 88.9 microns | 3.50 mil | Side 1; Arlon SQA-TMS-003 | |||
| 88.9 microns | 3.50 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | S | |||
| 381 microns | 15.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 39 | 39 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.93 MPa | 860 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 720 % | 720 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 20.2 kN/m | 115 pli | Silicone Property; ASTM D624 | ||
| Peel Strength | 1.30 kN/m | 7.40 pli | Bond Strength; Arlon SQA-TMS-029 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 16.2 | Arlon SQA-TMS-025 | |||