| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 38.1 microns | 1.50 mil | Polyethylene Interleave | ||
| 76.2 microns | 3.00 mil | Prime Coated 113 Fiberglass, Substrate | |||
| 152 - 203 microns | 6.00 - 8.00 mil | Side 1 | |||
| 279 - 330 microns | 11.0 - 13.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | 5.90 - 7.205 MPa | 855 - 1045 psi | Compound Property | ||
| Elongation at Break | 340 - 410 % | 340 - 410 % | Compound Property | ||
| Peel Strength | >= 0.526 kN/m | >= 3.00 pli | [ppi], Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 232 °C | 2.00 hour @Temperature 450 °F | Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month @Temperature <=23.9 °C | 6.00 Month @Temperature <=75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 10 - 14 | ||||
| Uncoated Fabric Break Strength | 150 lb/in | Warp Direction, Substrate Property | |||
| 70 lb/in | Fill Direction, Substrate Property | ||||