- 密度 [g/cm3]: 1.47
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 50.8 microns | 2.00 mil | Side 2; Arlon SQA-TMS-003 | ||
| 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 63.5 microns | 2.50 mil | Interleave | |||
| 76.2 microns | 3.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 178 microns | 7.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 66 | 66 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 275 % | 275 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 0.701 kN/m | 4.00 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 0.60 | 0.60 | [in], Flame Propagation | ||
| 0.70 | 0.70 | [sec], After Flame Time | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| White | Substrate | ||||
| Total Product Weight (oz/yd2) | 8.2 | Arlon SQA-TMS-025 | |||