- 密度 [g/cm3]: 2.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.80 g/cc | 0.101 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 38.1 microns | 1.50 mil | Liner 1 | ||
| 38.1 microns | 1.50 mil | Liner 2 | |||
| 76.2 microns | 3.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 152 microns | 6.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 152 microns | 6.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 381 microns | 15.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 77 | 77 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 4.72 MPa | 685 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 125 % | 125 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.0245 GPa @Strain <=1.00 % | 3.55 ksi @Strain <=1.00 % | Silicone Property; Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Shear Modulus | 0.000296 GPa @Strain <=25.0 % | 0.0430 ksi @Strain <=25.0 % | ASTM D1002 | ||
| Shear Strength | 6.05 MPa | 878 psi | Lap; ASTM 1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 6.91 @Frequency 1.00e+6 Hz | 6.91 @Frequency 1.00e+6 Hz | Silicon Property; IPC TM 650 - 2.5.5.3 | ||
| Dielectric Strength | 34.7 kV/mm | 882 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.0044 @Frequency 1.00e+6 Hz | 0.0044 @Frequency 1.00e+6 Hz | Silicon Property; IPC TM 650 - 2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 160 °C | 6.11 µin/in-°F @Temperature 68.0 - 320 °F | Silicone Property; ASTM E 831 | ||
| Specific Heat Capacity | 0.820 J/g-°C @Temperature 100 °C | 0.196 BTU/lb-°F @Temperature 212 °F | Silicone Property; Arlon SQA-TMS-052 | ||
| Thermal Conductivity | 1.40 W/m-K @Temperature 100 °C | 9.72 BTU-in/hr-ft²-°F @Temperature 212 °F | Silicone Property; ASTM E 1530 | ||
| 1.50 W/m-K @Pressure 30.0 MPa, Temperature 50.0 °C | 10.4 BTU-in/hr-ft²-°F @Pressure 4350 psi, Temperature 122 °F | Product Property; Arlon SQA-TMS-054 | |||
| Maximum Service Temperature, Air | 95.6 °C | 204 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | -118 °C | -180 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 121 °C | 0.250 hour @Temperature 250 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.00 - 10.0 °C | 6.00 Month @Temperature 39.2 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Plasticity | 2.3 mm | Arlon-SQA-TMS-005 | |||
| Total Product Weight (g/m2) | 550 | Arlon SQA-TMS-025 | |||