Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Thickness | >= 63.5 microns | >= 2.50 mil | Side 1 | ||
>= 63.5 microns | >= 2.50 mil | Side 2 | |||
76.2 microns | 3.00 mil | Polyethylene, Interleave | |||
203 microns | 8.00 mil | Prime Coated 7628 Fiberglass, Substrate | |||
343 - 419 microns | 13.5 - 16.5 mil | Overall | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 55 | 55 | Compound Property | ||
Tensile Strength | >= 4.83 MPa | >= 700 psi | Compound Property | ||
Elongation at Break | >= 200 % | >= 200 % | Compound Property | ||
Peel Strength | >= 0.877 kN/m | >= 5.00 pli | Bond Strength | ||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | 15.7 kV/mm | 400 kV/in | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 232 °C | 450 °F | |||
Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
Shelf Life | 6.00 Month @Temperature 18.3 - 23.9 °C | 6.00 Month @Temperature 65.0 - 75.0 °F | From date of manufacture | ||
Descriptive Properties | |||||
Color | Red | ||||
Total Product Weight (oz/yd2) | 14.7 - 17.7 | ||||
Uncoated Fabric Break Strength | 200 lb/in | Fill Direction, Substrate Property | |||
250 lb/in | Warp Direction, Substrate Property |