- 密度 [g/cm3]: 1.22
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.22 g/cc | 0.0441 lb/in³ | Side 2, Silicone Property; Arlon SQA-TMS-024 | ||
1.33 g/cc | 0.0480 lb/in³ | Side 1, Silicone Property; Arlon SQA-TMS-024 | |||
Thickness | 76.2 microns | 3.00 mil | Side 1; Arlon SQA-TMS-003 | ||
76.2 microns | 3.00 mil | Interleave | |||
229 microns | 9.00 mil | Side 2; Arlon SQA-TMS-003 | |||
457 microns | 18.0 mil | Substrate; Arlon SQA-TMS-003 | |||
762 microns | 30.0 mil | Overall; Arlon SQA-TMS-003 | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 36 | 36 | Side 2, Silicone Property; ASTM D2240 | ||
50 | 50 | Side 1, Silicone Property; ASTM D2240 | |||
Tensile Strength | 5.34 MPa | 775 psi | Side 1, Silicone Property; ASTM D412 | ||
6.38 MPa | 925 psi | Side 2, Silicone Property; ASTM D412 | |||
Elongation at Break | 325 % | 325 % | Side 1, Silicone Property; ASTM D412 | ||
550 % | 550 % | Side 2, Silicone Property; ASTM D412 | |||
Tear Strength | 8.77 kN/m | 50.0 pli | Side 1, Silicone Property; ASTM D624 | ||
14.5 kN/m | 83.0 pli | Side 2, Silicone Property; ASTM D624 | |||
Peel Strength | 4.38 kN/m | 25.0 pli | Bond Strength; ASTM D624 | ||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | 16.7 kV/mm | 425 kV/in | ASTM D149 | ||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 232 °C | 450 °F | |||
Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
Descriptive Properties | |||||
Color | Red | ||||
Total Product Weight (oz/yd2) | 28.5 | Arlon SQA-TMS-025 |