- 密度 [g/cm3]: 1.38
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 127 microns | 5.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 152 microns | 6.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 737 microns | 29.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Outgassing - Total Mass Loss | 0.10 % | 0.10 % | Post Cured - CVCM; ASTM E 595 | ||
| 0.28 % | 0.28 % | Cured - CVCM; ASTM E 595 | |||
| 0.34 % | 0.34 % | Post Cured - TML; ASTM E 595 | |||
| 1.07 % | 1.07 % | Cured - TML; ASTM E 595 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 48 | 48 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.86 MPa | 850 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 450 % | 450 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 12.3 kN/m | 70.0 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 1.49 kN/m | 8.50 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 14.4 kV/mm | 365 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 218 °C | 2.00 hour @Temperature 425 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 18.3 - 23.9 °C | 6.00 Month @Temperature 65.0 - 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 28 | Arlon SQA-TMS-025 | |||