- 密度 [g/cm3]: 1.37
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 229 microns | 9.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.52 MPa | 800 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 300 % | 300 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.38 kN/m | 7.90 pli | (S1 to S2) Bond Strength | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 0.75 | 0.75 | [in], Char Length; FTMS 191A Method 5903 | ||
| 12.3 | 12.3 | [sec], Flame and Glow Time; FTMS 191A Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 138 °C | 0.250 hour @Pressure 50.0 psi, Temperature 280 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 26.8 | Arlon SQA-TMS-025 | |||