Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
457 microns | 18.0 mil | Prime Coated 162 Fiberglass, Substrate | |||
432 - 559 microns | 17.0 - 22.0 mil | Side 2 | |||
432 - 559 microns | 17.0 - 22.0 mil | Side 1 | |||
1450 - 1700 microns | 57.0 - 67.0 mil | Overall | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
Tensile Strength | 5.58 - 6.83 MPa | 810 - 990 psi | Compound Property | ||
Elongation at Break | 450 - 550 % | 450 - 550 % | Compound Property | ||
Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 232 °C | 450 °F | |||
Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length; FTMS 191A; Method 5903 | ||
<= 25 | <= 25 | [sec], Flame & Glow Time; FTMS 191A; Method 5903 | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
Descriptive Properties | |||||
Color | Red | ||||
Total Product Weight (oz/yd2) | 58.2 - 68.2 | ||||
Uncoated Fabric Break Strength | 420 lb/in | Fill Direction, Substrate Property | |||
700 lb/in | Warp Direction, Substrate Property |