| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 25.4 microns | 1.00 mil | Interleave: Release liner to be determined (Temporarily FEP Film) | ||
| 50.8 microns | 2.00 mil | K2030 PEN Film, Substrate | |||
| 25.4 - 76.2 microns | 1.00 - 3.00 mil | Side 1 | |||
| 76.2 - 127 microns | 3.00 - 5.00 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property | ||
| Elongation at Break | >= 600 % | >= 600 % | Compound Property | ||
| Peel Strength | >= 0.351 kN/m | >= 2.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 138 °C | 0.0833 hour @Pressure 50.0 psi, Temperature 280 °F | Recommended Cure Cycle | ||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Total Product Weight (oz/yd2) | 3 - 4.8 | ||||
| Uncoated Fabric Break Strength | 31900 lb/in | Warp Direction, Substrate Property | |||
| 31900 lb/in | Fill Direction, Substrate Property | ||||