| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 25.4 microns | 1.00 mil | Side 1 | ||
| 38.1 microns | 1.50 mil | Polyethylene, Interleave | |||
| >= 102 microns | >= 4.00 mil | Side 2 | |||
| 178 microns | 7.00 mil | Prime Coated 1628 Fiberglass, Substrate | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | 5.58 - 6.83 MPa | 810 - 990 psi | Compound Property | ||
| Elongation at Break | 450 - 550 % | 450 - 550 % | Compound Property | ||
| Peel Strength | >= 0.877 kN/m | >= 5.00 pli | Bond Strength (Rubber to Rubber) | ||
| >= 0.877 kN/m | >= 5.00 pli | Bond Strength (Rubber to Polyester) | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Descriptive Properties | |||||
| Color | Red | Side 2 | |||
| Silver | Side 1 | ||||
| Total Product Weight (oz/yd2) | 12 - 14 | ||||
| Uncoated Fabric Break Strength | 200 lb/in | Fill Direction, Substrate Property | |||
| 250 lb/in | Warp Direction, Substrate Property | ||||