| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | >= 63.5 microns | >= 2.50 mil | Side 1 | ||
| >= 63.5 microns | >= 2.50 mil | Side 2 | |||
| 76.2 microns | 3.00 mil | Polyethylene, Interleave | |||
| 88.9 microns | 3.50 mil | Prime Coated 2113 Fiberglass, Substrate | |||
| 191 - 292 microns | 7.50 - 11.5 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property | ||
| Elongation at Break | >= 500 % | >= 500 % | Compound Property | ||
| Peel Strength | >= 0.526 kN/m | >= 3.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | HB | HB | Compound Rated | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 7.1 - 8.9 | ||||
| Uncoated Fabric Break Strength | 175 lb/in | Warp Direction, Substrate Property | |||
| 70 lb/in | Fill Direction, Substrate Property | ||||