- 密度 [g/cm3]: 1.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 38.1 microns | 1.50 mil | Interleave 1 | ||
| 38.1 microns | 1.50 mil | Interleave 2 | |||
| 76.2 microns | 3.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 76.2 microns | 3.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.21 MPa | 900 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 150 % | 150 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.02 kN/m | 5.80 pli | Bond Strength; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 1.0 | 1.0 | [in], Char Length; FTMS 191A, Method 5903 | ||
| 2.0 | 2.0 | [sec], Flame/Glow; FTMS 191A, Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 177 °C | 0.0833 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 15 | Arlon SQA-TMS-025 | |||