- 密度 [g/cm3]: 1.17
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | Silicone Property, Side 1; Arlon SQA-TMS-024 | ||
| 1.23 g/cc | 0.0444 lb/in³ | Silicone Property, Side 2; Arlon SQA-TMS-024 | |||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 102 microns | 4.00 mil | Side 1 | |||
| 203 microns | 8.00 mil | Side 2 | |||
| 203 microns | 8.00 mil | Substrate | |||
| 508 microns | 20.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 43 | 43 | Silicone Property, Side 2; ASTM D2240 | ||
| 45 | 45 | Silicone Property, Side 1; ASTM D2240 | |||
| Tensile Strength | 5.34 MPa | 775 psi | Silicone Property, Side 2; ASTM D412 | ||
| 6.21 MPa | 900 psi | Silicone Property, Side 1; ASTM D412 | |||
| Elongation at Break | 325 % | 325 % | Silicone Property, Side 1; ASTM D412 | ||
| 425 % | 425 % | Silicone Property, Side 2; ASTM D412 | |||
| Peel Strength | 2.19 kN/m | 12.5 pli | Bond Strength; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Total Product Weight (oz/yd2) | 20.6 | Arlon SQA-TMS-025 | |||