- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| 1.70 g/cc | 0.0614 lb/in³ | Substrate Property; Arlon SQA-TMS-024 | |||
| Thickness | 50.8 microns | 2.00 mil | Substrate; Arlon SQA-TMS-003 | ||
| 76.2 microns | 3.00 mil | Liner | |||
| 381 microns | 15.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 432 microns | 17.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 18 | 18 | Silicone Property; ASTM D2240 | ||
| 67 | 67 | Substrate Property; ASTM D2240 | |||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| 41.4 MPa | 6000 psi | Substrate Property; ASTM D412 | |||
| Elongation at Break | 300 % | 300 % | Substrate Property; ASTM D412 | ||
| 950 % | 950 % | Silicone Property; ASTM D412 | |||
| Modulus of Elasticity | 0.000517 GPa | 0.0750 ksi | Silicone Property; ASTM E 831 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 31.1 kV/mm | 790 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 335 µm/m-°C | 186 µin/in-°F | Silicone Property; ASTM E 831 | ||
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 | ||
| Maximum Service Temperature, Air | 154 °C | 310 °F | |||
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.103 - 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 15.0 - 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.44 - 10.0 °C | 6.00 Month @Temperature 40.0 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Translucent | ||||
| Total Product Weight (oz/yd2) | 14.9 | Arlon SQA-TMS-025 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.