- 密度 [g/cm3]: 1.35
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 50.8 microns | 2.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 76.2 microns | 3.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 76.2 microns | 3.00 mil | Side 1 Interleave | |||
| 76.2 microns | 3.00 mil | Side 2 Interleave | |||
| 178 microns | 7.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.52 MPa | 800 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 225 % | 225 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 15.8 kN/m | 90.0 pli | Die B, Compound Property; ASTM D624 | ||
| Peel Strength | 0.841 kN/m | 4.80 pli | Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 35.4 kV/mm | 900 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Total Product Weight (oz/yd2) | 8 | Arlon SQA-TMS-025 | |||