- 密度 [g/cm3]: 1.11
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 457 microns | 18.0 mil | Overall; Arlon SQA-TMS-003 | ||
| 457 microns | 18.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | Interleave | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 | 40 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 8.62 MPa | 1250 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 800 % | 800 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 38.6 kN/m | 220 pli | Die B, Silicone Property; ASTM D624 | ||
| Compression Set | 19 % | 19 % | Arlon SQA-TMS-017 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 50.20 kV/mm | 1275 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 60.0 Month @Temperature 23.9 °C | 60.0 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Saddle Brown | ||||
| Total Product Weight (oz/yd2) | 15.1 | Arlon SQA-TMS-025 | |||