- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| 1.70 g/cc | 0.0614 lb/in³ | Substrate Property; Arlon SQA-TMS-024 | |||
| Thickness | 50.8 microns | 2.00 mil | Substrate; Arlon SQA-TMS-003 | ||
| 76.2 microns | 3.00 mil | Liner | |||
| 381 microns | 15.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 432 microns | 17.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 18 | 18 | Silicone Property; ASTM D2240 | ||
| 67 | 67 | Substrate Property; ASTM D2240 | |||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| 41.4 MPa | 6000 psi | Substrate Property; ASTM D412 | |||
| Elongation at Break | 300 % | 300 % | Substrate Property; ASTM D412 | ||
| 950 % | 950 % | Silicone Property; ASTM D412 | |||
| Modulus of Elasticity | 0.000517 GPa | 0.0750 ksi | Silicone Property; ASTM E 831 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 31.1 kV/mm | 790 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 335 µm/m-°C | 186 µin/in-°F | Silicone Property; ASTM E 831 | ||
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 | ||
| Maximum Service Temperature, Air | 154 °C | 310 °F | |||
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.103 - 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 15.0 - 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.44 - 10.0 °C | 6.00 Month @Temperature 40.0 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Translucent | ||||
| Total Product Weight (oz/yd2) | 14.9 | Arlon SQA-TMS-025 | |||