- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave 2 | ||
| 76.2 microns | 3.00 mil | Interleave 1 | |||
| 127 microns | 5.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Side 2; Arlon SQA-TMS-003 | |||
| 762 microns | 30.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 47 | 47 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 8.853 MPa | 1284 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 449 % | 449 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 18.9 kN/m | 108 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 4.58 kN/m | 26.1 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 31.9 kV/mm | 811 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 1.5 | 1.5 | [in], Char Length; FAR 25.853 App. F, P.1, S.Aii | ||
| 8.0 | 8.0 | [sec], Flame Time; FAR 25.853 App. F, P.1, S.Aii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Blue | Interleave 2 | |||
| Red | |||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 29 | Arlon SQA-TMS-025 | |||