| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 25.4 microns | 1.00 mil | Side 1 | ||
| 50.8 microns | 2.00 mil | Side 2 | |||
| 63.5 microns | 2.50 mil | Substrate | |||
| 140 microns | 5.50 mil | Overall Thickness | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | Compound Property | ||
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property | ||
| Elongation at Break | >= 550 % | >= 550 % | Compound Property | ||
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 232 °C | 2.00 hour @Temperature 450 °F | Recommended Post Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 5 | ||||
| Uncoated Fabric Break Strength (lb/in) | 40 | Fill Direction, Substrate Property | |||
| 70 | Warp Direction, Substrate Property | ||||